The effect of alcoholic solutions on the thermomechanical properties of immersed poly(lactic acid) films

Updated from an original article written by Rafael Auras.

The effects of aqueous and deuterium oxide (D2O) solutions of alcohols (methanol, ethanol, 1-propanol, 2-propanol, and 1-butanol) on the thermomechanical properties of poly(lactic acid)—PLA—films were assessed by dynamic mechanical analysis.

Immersion of PLA in alcohol solution and effect of Tg.

The effect of alcoholic solutions on the thermomechanical properties of immersed poly(lactic acid) films

The effects of aqueous and deuterium oxide (D2O) solutions of alcohols (methanol, ethanol, 1-propanol, 2-propanol, and 1-butanol) on the thermome- chanical properties of poly(lactic acid)—PLA—films were assessed by dynamic mechanical analysis. The glass transition temperature (Tg) of PLA films immersed in 25%, 50%, 75%, and 100% (v/v) alcoholic solutions were compared with the Tg of films immersed in 100% water and D2O. The Tg of PLA films immersed in methanol and ethanol aqueous solutions decreased as the con- centration of the alcohol solutions increased. For methanol and ethanol, the Tg decreased by 8.6 and 7.6C per 25% (v/v) increase in alcohol, respectively. When the PLA films were immersed in propanol aqueous solutions and buta- nol, the Tg reached the lowest value at 75% (v/v) and 100% (v/v), respectively. Tg of PLA films immersed in 1-propanol and 2-propanol decreased by 8.6 and 8.9C for every 25% increase in propanol before reaching the minimum value, respectively. Aqueous and D2O solutions had similar effects on Tg. Selective studies of crystallinity evolution, ethanol sorption, degree of swelling, and Hansen solubility parameters of PLA were conducted. This work assists in developing PLA films intended for contact with aqueous-alcoholic solutions.

Did you find this article useful?

You Might Also Be Interested In

Tag List
  • auras lab,
  • canr,
  • packaging,
  • school of packaging
Michigan State University
  • Spartans Will.
  • © Michigan State University

MSU is an affirmative-action, equal-opportunity employer, committed to achieving excellence through a diverse workforce and inclusive culture that encourages all people to reach their full potential.

Michigan State University Extension programs and materials are open to all without regard to race, color, national origin, gender, gender identity, religion, age, height, weight, disability, political beliefs, sexual orientation, marital status, family status or veteran status. Issued in furtherance of MSU Extension work, acts of May 8 and June 30, 1914, in cooperation with the U.S. Department of Agriculture. Quentin Tyler, Director, MSU Extension, East Lansing, MI 48824. This information is for educational purposes only. Reference to commercial products or trade names does not imply endorsement by MSU Extension or bias against those not mentioned.

The 4-H Name and Emblem have special protections from Congress, protected by code 18 USC 707.

We comply with the Federal Trade Commission 1998 Children’s Online Privacy Protection Act (COPPA).